| 摘要 |
The invention relates to a method for producing non-grain-oriented hot-rolled magnetic steel sheet in which from a raw material such as cast slabs, strip, roughed strip or thin slabs produced from a steel comprising (in weight %) C: 0.0001-0.05 %; Si: <=1.5 %; Al: <=0.5 %, wherein [% Si]+2[% Al]<=1.8; Mn: 0.1-1.2 %; if necessary up to a total of 1.5 % of alloying additions such as P, Sn, Sb, Zr, V, Ti, N, Ni, Co, Nb and/or B, with the remainder being iron and the usual impurities, in a finishing roll line at temperatures above the Ar1 temperature, a hot strip with a thickness <=1.5 mm is rolled, wherein at least the last forming pass of hot rolling is carried out in the mixed region austenite/ferrite and wherein the total deformation epsilH achieved during rolling in the mixed region austenite/ferrite is <35 %. With the method according to the invention, it is possible in particular to economically produce thicker magnetic steel sheet which is not grain-oriented and which has good magnetic properties. |