| 摘要 |
To 100 parts by weight of crushued rubber chips having a particle size of from 1 to 10 mm or fibrous rubber chips having a fibrous length of 30 mm or below are added a film forming material, which contains a pigment and 10 to 100 parts by weight of a one-pack type or two-pack type polyurethane resin which gels at least from a liquid state in 60 seconds or more and cures through the gelling process, and they are stirred for mixing. When the polyurethane resin starts to gel and the rubber chips start to aggregate, stirring is further continued for mixing in spite of heavy load on the mixer so to loosen the aggregation of the rubber chips. By configuring as described above, A manufacturing method which can form a thick colored film without requiring a complex procedure and can inexpensively obtain colored rubber chips which have a remarkable color keeping property and a pyramid shape with edges similar to those formed when crushed is provided. |