| 摘要 |
The present invention relates to a molding material for OA machine parts, wherein such material comprises a resin combination of 60 to 98 parts by weight of a polyphenylene ether-based resin, 2 to 40 parts by weight of a thermoplastic elastomer, and 1 to 50 parts by weight of a flame retardant, such that the resin composition has a bending modulus of not less than 1500 MPa as measured at 23° C. according to ASTM D790, a damping ratio of not less than 1.0% at 23° C., and a thermal deformation temperature of not less than 100° C. as measured according to ASTM D648 under 18.6 kg/cm2 load, and wherein the product of the bending modulus and the damping ratio is not less than 10,000 MPa*%.
|