摘要 |
A graft copolymer of a propylene polymer material is prepared by (1) making an oxidized propylene polymer material by (a) irradiating a porous particulate propylene polymer material in the substantial absence of oxygen, (b) exposing the irradiated propylene polymer material to a controlled amount of oxygen of greater than 0.004% but less than 15% by volume at a temperature of 40.degree. to 110.degree.C, and (c) heating th e irradiated polymer material to a temperature of at least 110.degree.C in the presence of a contolled amount of oxygen within the same range as is used in the previous step, (2) dispersing the resulting oxidized propylene polymer material in water in the presence of a surfactant at a temperature o f 30.degree.-90.degree.C, (3) adding (a) a primary reducing agent, (b) a chelating agent, and (c) a secondary reducing agent, (4) adding at least one vinyl monomer, and (5) recovering the graft copolymer from the reaction mixture.
|