A high-hardness martensitic stainless steel excellent in corrosion resistance, comprising less than 0.15% by weight of C, from 0.10 to 1.0% by weight of Si, from 0.10 to 2.0% by weight of Mn, 0.010% or less of S, from 12.0 to 18.5% by weight of Cr, from 0.40 to 0.80% by weight of N, less than 0.030% by weight of Al, less than 0.020% by weight of O, and substantially the balance of Fe. The martensitic stainless steel of the present invention has cold-workability and hardness after tempering higher than that of SUS420J2 and corrosion resistance equivalent to or higher than that of an austenitic stainless steel SUS316.
|