| 摘要 |
<p>The invention concerns steel for high temperature use containing by weight: 0.06 to 0.20% of C, 0.10 to 1.00% of Si, 0.10 to 1.00% of Mn, not more than 0.010% of S, 10.00 to 13.00% of Cr, not more than 1.00% of Ni, 1.00 to 1.80% of W, Mo such that (W/2+Mo) is not more than 1.50%, 0.50 to 2.00% of Co, 0.15 to 0.35% of V, 0.040 to 0.150% of Nb, 0.030 to 0.12% of N, 0.0010 to 0.0100% of B and optionally up to 0.0100% of Ca, the rest of the chemical composition consisting of iron and impurities or residues resulting from or required for preparation processes or steel casting. The chemical constituent contents preferably verify a relationship such that the steel after normalizing heat treatment between 1050 and 1080°C and tempering has a tempered martensite structure free or practically free of δ ferrite.</p> |