| 摘要 |
Lead brass components for potable water distribution circuits (e.g., plumbing components made of CuZn39Pb3, containing 3% Pb), also chronium plated ones, are subjected to a lead-selective surface etching to reduce, in operation, the release of Pb caused by Pb surface "smearing", resulting either from machining or molding; said elements are firstly contacted by an aqueous solution of an acid capable of forming soluble Pb salts, preferably a non-oxidizing solution, by simply dipping the components in the solution, e.g., a solution of 0.1 M sulfamic acid, at 20°-50° C. for 10 to 50 minutes, and, subsequently, the elements are passivated by immersion into a strong base aqueous solution, e.g., a solution of 0.1 M NaOH at 20°-25° C., for approximately 10 minutes; in this manner, plumbing components made of a copper based alloy containing Pb are obtained, which components, after 15 days of test according to US NSF STD61 procedure, release Pb in an amount less than 0.025 mug for each ml of the internal volume of the component delimited by metallic walls remained in contact with water during the testing period.
|