NANOSCALE CORUNDUM POWDERS, SINTERED COMPACTS PRODUCED FROM THESE POWDERS AND METHOD FOR PRODUCING THE SAME

摘要

Nanoscale corundum powders are obtained by first producing an Al2O3 precursor by adding seed crystals to an aqueous solution of an aluminium compound and adding a base and then converting the Al2O3 precursor into corundum by calcination at a high temperature. Before the calcination, the salts that are present in addition to the Al2O3 precursor are separated off. The resulting product is calcinated at temperatures of 700 to 975 DEG C and any fines that may be present are removed. The resulting corundum powders can be sintered at temperatures ≤ 1200 DEG C to produce compacts or components of multiple layer systems.