| 摘要 |
PROBLEM TO BE SOLVED: To provide a joining method for a metal-ceramic composite material by which joining is easily and firmly performed even in the atmosphere, and its joined body. SOLUTION: In the joining method for the metal-ceramic composite material, lead borate glass containing >=50% to <100% PbO by weight is loaded between the metal-ceramic composite material using an Al alloy as a matrix and the same kind or different kind of a material as or from it, the loaded part is heated in the atmosphere at a temperature of 300 deg.C or more and not more than a melting point of metal in a composite material and is joined while placing a load not more than 0.1 MPa on the loaded part, and to provide the joined body manufactured by the method.
|