The magnetic powder is composed of an alloy composition represented by Rx(Fe1-aCoa)100-x-y-zByMz (where R is at least one kind of rare-earth element excepting Dy, M is at least one kind of element selected from Ti, Cr, Nb, Mo, Hf, W, Mn, Zr and Dy, x is 7.1 - 9.9at% , y is 4.6 - 8.0at%, z is 0.1 - 3.0at%, and a is 0 - 0.30, and the magnetic powder being constituted from a composite structure having a soft magnetic phase and a hard magnetic phase, wherein when the magnetic powder is mixed with a binding resin and then the mixture is subjected to compaction molding to form a bonded magnet having a density rho ÄMg/m<3>Ü, the maximum magnetic energy product (BH)maxÄkJ/m<3>Ü of the bonded magnet at a room temperature satisfies the relationship represented by the formula (BH)max/ rho <2> Äx10<-9>Jm<3>/g<2>Ü ≥ 2.40, and the intrinsic coercive force Hcj of the bonded magnet at a room temperature is in the range of 400 - 750kA/m. |