| 摘要 |
A process for preparing a polyhydroxycarboxylic acid having a weight average molecular weight of 50,000 to 1,000,000, which comprises a crystallizing step comprising (A) a step of heating pellets of a polyhydroxycarboxylic acid having a weight average molecular weight of 2,000 to 100,000 under stirring to a temperature from glass transition point or higher to a melting point or lower and heating until a defined result is attained, and (B) a step of heating the polyhydroxycarboxylic acid to a temperature of solid phase polycondensation reaction temperature, and a solid phase polycondensation reaction step of reacting the crystallized polyhydroxycarboxylic acid at an endothermic start temperature or lower of an endothermic peak as recognized upon temperature elevation analysis of the crystallized polyhydroxycarboxylic acid by using a differential scanning calorimeter.
|