A roller bearing which can sufficiently ensure an endurance life of rollers even under conditions where debris contamination and temperature rise are large. As the material for an outer ring, inner ring and tapered rollers, a steel in which the Si and-Mn contents are increased is used, and after it has been treated to carbo-nitriding, it is quenched to adjust the amount of retained austenite in the carbo-nitrided layer formed on the surface layer of each part to 20-50 vol %. Thus, it is possible to prevent surface peeling resulting from initiation and propagation of cracks,. thereby greatly improving the endurance life of the rolling bearing under conditions in which debris contamination or temperature rise at bearing portions is large.
|