PROBLEM TO BE SOLVED: To suppress characteristics variation between a dielectric ceramic layer and a magnetic ceramic layer, caused by the mutual dispersion of the components of the ceramic layers and, at the same time, to obtain a proper joined state between the ceramic layers in a sintered laminate, even when the sintered laminated body is formed by laminating a green dielectric ceramic layer and a green magnetic ceramic layer upon another, without interposing an intermediate layer in between and baking the green laminate so as to obtain chip-like composite LC components. SOLUTION: In the green laminate 4a, from which the sintered laminate having a laminated structure prepared for the composite LC parts is obtained through baking, crystallized glass the viscosity of which drops by crystal melting in the temperature range from the sintering start temperature to the sintering end temperature, in the step of baking a green dielectric ceramic layer 5a and a green magnetic ceramic layer 6a is added to at least either one of the layers 5a and 6a. |