| 摘要 |
A method of continuously loading fibers in a fiber suspension with calcium carbonate. The fibers include a fiber wall surrounding a lumen. A reactant solid in the form of calcium oxide and/or calcium hydroxide is mixed into the fiber suspension with a resultant initial process pH of between 11 and 12. The fiber suspension is transported at a consistency of between approximately 15 and 30% into an inner chamber of a closed reactor. A reactant gas is injected into the reactor, whereby the reactor is pressurized to a pressure between 5 and 150 psi. A temperature of the fiber suspension within the reactor is controlled at a range between -10° C. and 80° C. The fibers within the fiber suspension are loaded with calcium carbonate as a result of a chemical reaction between the reactant solid and the reactant gas in the reactor over a predetermined reaction time. A specific type of calcium carbonate crystals are grown on the fiber walls of the fibers, depending upon the initial process pH, temperature, pressure and reaction time.
|