A process for producing aliphatic polyester wherein a crystallized aliphatic polyester prepolymer formed from an aliphatic dihydric alcohol and an aliphatic dicarboxylic acid and having a weight-average molecular weight of 2,000 to 100,000 is caused to undergo solid-phase polymerization in the presence of a volatile catalyst to make an aliphatic polyester having a weight-average molecular weight of 50,000 to 1,000,000. This process is more efficient than any prior process calling for a complicated step for catalyst removal, since it enables the removal of the catalyst from the reaction system during and/or after solid-phase polymerization. The polyester is comparable in stability to any aliphatic polyester having any catalyst removed therefrom.
|