The invention relates to a higher-strength steel strip or steel sheet comprising a predominantly ferritic-martensitic microstructure with a martensite content of between 4 and 20%, wherein the steel strip or steel sheet, apart from Fe and impurities due to smelting, comprises (in % by weight) 0.05-0.2% C, <=1.0% Si, 0.8-2.0% Mn, <=0.1% P, <=0.015% S, 0.02-0.4% Al, <=0.005% N, 0.25-1.0% Cr, 0.002-0.01% B. Preferably the martensite content is approximately 5% to 20% of the predominantly martensitic-ferritic microstructure. Such a higher-strength steel strip or steel sheet made from a dual phase steel comprises good mechanical/technological properties even after being subjected to an annealing process which includes an overageing treatment. Furthermore, the invention relates to a method for producing steel strip or steel sheet according to the invention. |