| 摘要 |
<p>A vacuum switch container, a vacuum switch, a method of producing the vacuum switch container and a method of producing the vacuum switch are provided. Ceramic granulated powders were filled in a space in a cylindrical shape defined by an outer mold made of hard metal having an inner diameter of 120 mm and a center pin made of hard metal having an outer diameter of 108 mm and applied with a pressure of 1000 kg/cm<2> in a radial direction of the cylindrical shape by using a lower punch and an upper punch, both of which are in a similar cylindrical shape, from both of a top and a bottom of the space in a cylindrical shape to produce a green compact. Next, the green compact was fired in an open air at 1600 DEG C to produce a ceramic fired body in a cylindrical shape. Next, each of end surfaces of the ceramic fired body was ground. Next, metalizing was performed on the thus ground surface. Further, Ni plating was applied on the metalized surface thereby forming an electroconductive layer thereon to complete the vacuum switch container. <IMAGE></p> |