| 摘要 |
PROBLEM TO BE SOLVED: To provide a surface protective laminated film capable of molding a stable film without wrinkle at a film production time and without elongation or breakage of the laminated film at print laminating time without necessity of a solvent, heat adhering at a low temperature without necessity of an anchor coating agent coating at an extrusion laminating time and having no discoloring of a printing ink, no curl and improved cutting properties of the laminated film. SOLUTION: The surface protective laminated film comprises (A) a propylene polymer resin layer containing anα-olefin content of 0 to 5 wt.% and an MFR of 1 to 100 g/10 min and contacted with one side surface of a propylene resin film base, and (B) a linear ethyleneα-olefin copolymer resin layer having a density of 0.870 to 0.910 g/cm3 and an MFR of 1 to 100 g/10 min and laminated on the resin layer (A).
|