Porous polypropylene film, process for producing the same, and absorbent articleemploying the film

摘要

Disclosed is a porous film made of a resin composition containing (I) (i) a propylene-ethylene copolymer or (ii) a polypropylene-based resin mixture containing a propylene-ethylene copolymer, each having an ethylene content of 3.0 to 7.0 wt.% and an MFR measured at 230 DEG C of 2.0 to 4.0 g/10 min and (II) a beta -crystal nucleating agent; the film having a porosity of 20 to 80%, a Gurley air permeability of 5,000 sec/100 cc or lower as measured according to JIS P-8117, a water vapor permeability of 2,000 g/m<2>.24h or higher as measured according to JIS Z-0208 and a water pressure resistance of 75 kPa or higher as measured according to JIS L-1092 using an aqueous surfactant solution; a process for producing the same; and an absorbent article employing the porous film as a backsheet.