| 摘要 |
The glasses used for making rigid disk substrates have the following composition (in % by weight based on oxides): SiO2, 40 to 50.8; Al2O3, 5 to 20; B2O3, 0 to 5; Li2O, 0 to 10; Na2O, 0 to 12, with the proviso that Li2O+Na2O, 5 to 12; K2O, 0 to 5; MgO, 0 to 20; CaO, 0 to 6, with the proviso that MgO+CaO, 4 to 20; SrO+BaO, 0 to 10; ZrO2, 0 to 5; TiO2,0 to 5; CeO2, 0 to 1; La2O3, 0 to 10; Fe2O3, 0 to 10; Nb2O5, 0 to 10; V2O5, 0 to 15, with the proviso that TiO2+ZrO2+La2O3+Fe2O3+Nb2O5+V2O5>=18.7; As2O3+Sb2O3+F. 0,1 to 1. These glasses also fulfill the following inequality formulae (1):wherein R represents the relaxation rate of the glass and E/rho represents specific elasticity modulus of the glass measured in GPA*cm3/g.
|