| 摘要 |
A method for producing agglomerated boron carbide, including the steps of providing a boron carbide powder precursor having particle sizes smaller than about 1 micron in diameter, mixing the boron carbide powder precursor with binder solution to form a slurry, drying the slurry to yield a solid residue, crushing the solid residue to yield green boron carbide particles, and firing the green boron carbide particles. The resultant agglomerated boron carbide particles have diameters generally ranging from about 5 to about 20 microns. The agglomerated boron carbide particles are characterized as boron carbide grains of about 1-2 microns in diameter suspended in a vitreous boron oxide matrix. |