PROCESS FOR MEASUREMENT OF THE DEGREE OF CURE AND PERCENT RESIN OF FIBERGLASS-REINFORCED EPOXY RESIN PREPREG

摘要

The degree of cure and the amount of epoxy resin in a fiberglass reinforced epoxy resin prepreg is measured by exposing the prepreg to a series of light pulses created by optical filters transmitting light at predetermined bandwidths about selected wavelengths, preferably centered at wavenumbers of about 4529 cm<-1> and 4055 cm<-1> and measuring the amount of epoxy groups and methyl groups present relative to reference values from the electrical pulses produced by a phase sensitive photoelectric detector disposed to receive said light pulses after being exposed to said prepreg. When such measurements are made in a continuously moving sheet of prepreg, it is possible to control the variation of percent cure and resin content to no greater than +/-3 % cure and +/-3 % resin content over a distance of at least 400 yds (366m).