Quick plastic forming of aluminum alloy sheet metal

摘要

A method is disclosed for stretching magnesium-containing aluminum alloy sheet stock into intricate shapes such as are required in automotive body panels. The sheet stock, at a temperature in the range of about 400° C. to about 510° C., is stretched under the pressure of a working gas into conformance with the surface of a forming tool. The sheet forming pressure is increased continually in a controlled manner from ambient pressure to a final forming level in the range of about 250 psi to about 500 psi or higher. A portion of the sheet can experience strain rates substantially higher than 10-3 sec-1 and the forming of the sheet can be completed within 12 minutes.