| 摘要 |
The invention provides a cast iron alloy comprising 3.0-3.8% carbon, 06-25% silicon, 0.2-0.65% manganese, 0.01-0.1% tin, <0.025% sulfur, 0.001-0.020% magnesium, 0.1-1.2% copper, 0.04-0.2% chromium, and balance up to 100% of iron and incidental impurities. The matrix structure is a continously variable ferrite/pearlite mixture and the content of carbides is less than 1%. The graphite shape of the alloy is 1 50% flake graphite, 50-99% compacted graphite and at most 10% spheroidal graphite. Such an alloy is easier to machine and less prone to shrinkage than an ordinary compacted graphite cast iron. |