| 摘要 |
Alumina particles having high dispersibility and plasticity, at least on the surface of which a phosphoric acid or phosphate is present and suitable for use as a material for pigments for paints, precision abrasives or ceramics. The alumina particles are produced by adding a crystallization inhibitor containing at least phosphate ion to aluminum hydroxide or alumina hydrate and then conducting a hydrothermal synthesis treatment. The amount of the phosphate ion to be added is in the range of 3.0x10-3 to 2.5x10-2 mol per mol of aluminum hydroxide or alumina hydrate. The particle size of aluminum hydroxide or alumina hydrate is 0.1 to 5.0 mum. The hydrothermal synthesis is preferably conducted at 350° C. or above under a pressure of 50 to 200 atm and at a temperature elevation rate of 5° C./min to 0.3° C./min. The thus obtained alumina is alpha-alumina in the form of hexagonal plate single crystal having a particle size of 0.2 to 15 mum, an aspect ratio of 15 to 50 and an isoelectric point at which the zeta-potential is 0 of pH 4 to 8.
|