Non-aqueous electrochemical cells with improved performance can be fabricated by employing anodes comprising a composition having graphite particles that have a BET method specific surface area of about 6 to about 12 m2/g and a crystallite height Lc of about 100 nm to about 120 nm, and wherein at least 90% (wt) of the graphite particles are less than 16 mum in size; a cathode; and a non-aqueous electrolyte containing a solvent and salt that is interposed between the anode and cathode. When employed in an electrochemical cell, the anode can attain a specific electrode capacity of at least 300 mAhr/g. The electrochemical cell has a cycle life of greater than 1500 cycles, and has a first cycle capacity loss of only about 10% to about 15%.
|