发明名称 |
POLYETHYLENE NAPHTHALATE RESIN MOLDED ARTICLE AND PRODUCTION THEREOF |
摘要 |
<p>PROBLEM TO BE SOLVED: To produce a resin molded article that will not develop crazing when stored in ethyl acetate at a specified temperature for a specified period of time by using a polyester resin composed of a naphthalenedicarboxylic acid as a main acid component and ethylene glycol as a main glycol component. SOLUTION: A polyethylene naphthalate(PEN) resin molded article comprises a polyester resin composed of a naphthalenedicarboxylic acid as a main acid component and ethylene glycol as a main glycol component and will not develop crazing when stored in ethyl acetate at 40 deg.C for 12 hr. For example, the PEN resin molded article is produced by feeding a PEN resin into an injection molding machine to form a preform and heat treating a molded article produced by e.g. blow molding the preform after heating, preferably at a temperature of 50-120 deg.C for not less than 0.1 hr. Alternatively, it is preferable to produce a PEN resin molded article at a mold temperature of 50-120 deg.C. The PEN resin molded article is useful as a container for storing the contents including an organic solvent such as a bottle for nail color or the like.</p> |
申请公布号 |
JP2001040101(A) |
申请公布日期 |
2001.02.13 |
申请号 |
JP20000073559 |
申请日期 |
2000.03.16 |
申请人 |
KANEBO LTD;KANEBO SYNTHETIC FIBERS LTD |
发明人 |
ITO YUMI;HASHIMURA TETSUTARO;YAMAMOTO MASAKI |
分类号 |
B65D1/00;B29C49/64;B29C71/02;B29K67/00;B29L22/00;B65D1/09;C08J5/00;C08J7/00;(IPC1-7):C08J5/00 |
主分类号 |
B65D1/00 |
代理机构 |
|
代理人 |
|
主权项 |
|
地址 |
|