| 摘要 |
<p>The present invention relates to a high fluidible, impact resistant conductive acrylonitrile-butadiene-styrene terpolymer material and a preparing method thereof. Said material has the following formula (weight percent): ABS 60∩65, carbon black 15∩25, impact modifier 15∩20, antioxidant 0.1∩0.2, UV absorbent agent 0.2∩0.3. All components with the above mentioned content were put into a high speed mixer to mix together, and then extruded with a twin screw extruder, the feed extruded were cooled with water, and then pulverised and dried to obtain the final product. Compared with the prior art, product of the present invention have the advantages of high fluidity, high impact resistance, and is conductive.</p> |