| 摘要 |
PURPOSE: In the manufacture of Fe-Mn alloy anode for use in continuous electroplating process, the Mn content is controlled to be 7-25wt.% and Al content is controlled to be 0.01- 0.5wt.% in Fe-Mn alloy. Therefore, uniform dissolution of anode surface during electrolysis is possible. CONSTITUTION: The manufacturing method of Fe-Mn alloy anode includes the steps of melting a Fe-Mn alloy containing 7-25wt.% of Mn; adding 0.01-0.5wt.% of Al to the molten Fe-Mn alloy; electrolysing above alloy at a current density of 100A/dm¬2 for 5 hours; and molding the electrolyzed alloy.
|