| 摘要 |
An ultra-high strength, weldable, low alloy, triple phase steel with excellent cryogenic temperature toughness in the base plate and in the heat affected zone (HAZ) when welded, having a tensile strength greater than about 830 MPa (120 ksi) and a microstructure comprising a ferrite phase, a second phase of predominantly lath martensite and lower bainite, and a retained austenite phase, is prepared by heating a steel slab comprising iron and specified weight percentages of some or all of the additives carbon, manganese, nickel, nitrogen, copper, chromium, molybdenum, silicon, niobium, vanadium, titanium, aluminum, and boron; reducing the slab to form plate in one or more passes in a temperature range in which austenite recrystallizes; further reducing the plate in one or more passes in a temperature range below the austenite recrystallization temperature and above the Ar3 transformation temperature; finish rolling the plate between the Ar3 transformation temperature and the Ar1 transformation temperature; quenching the finish rolled plate to a suitable Quench Stop Temperature (QST); and stopping the quenching.
|