RESIN COMPOSITION, MOLDED ARTICLE THEREOF, AND PROCESS FOR PRODUCING RESIN COMPOSITION

摘要

A resin composition obtained by mixing 4-52 mass% of fluororesin particles with an average particle diameter of 0.01-300 mu m and 48-96 mass% of polyether imide exhibits excellent flowability when thermally plasticized, is molded by injection molding, and can provide molded articles with excellent electrical characteristics, heat resistance, and plating characteristics. The resin composition can be prepared by a process comprising: dissolving the polyether imide in chloroform to a concentration of 10-500 g/L, dispersing the fluororesin particles in the resulting solution in an amount so that the ratio of the polyether imide and the fluororesin particles is in the range from 15:85 to 85:15 mass%, evaporating the solvent to obtain a preliminary mixture with an average particle diameter of 0.1-500 mu m, further adding the polyether imide, and blending the mixture.