| 摘要 |
The castable refractory material comprising as binders, per 100 parts by weight of solid components, (a) 10-30 parts by weight of water-inactive, fine refractory powder, which is a mixture of fine refractory powder having an average diameter of 0.2-0.6 .mu.m and fine refractory powder having an average diameter of 1-10 .mu.m at a ratio of 1:2-2:1; (b) 2-7 parts by weight (as an effective amount) of alumina cement having an average diameter of 3-8 .mu.m, cement clinker minerals thereof comprising CaO 12CaO index of the 12CaO or less assuming that the diffraction intensity index of the CaO at a lattice plane distance D of 2.96 .ANG. is 100; and (c) 0.4-3 parts by weight of fine amorphous silica powder having an average diameter of 0.5 .mu.m or less; the balance of the solid components being substantially refractory aggregate and refractory powder.
|