| 摘要 |
PROBLEM TO BE SOLVED: To suppress yellow coloring with a silver colloid without polishing surface by regulating the contents of Na2O, K2O and Li2O to specific values or above, regulating specific gravity to a specified value or below and providing a float glass having a specified absorbance. SOLUTION: This float glass is obtained by regulating the sum total of the contents of NaO, K2O and Li2O to >=5 wt.%, the specific gravity to <=2.7 at 20 deg.C and <=0.08 absorbance calculated by A=-log10(T/Tref) based on the transmittance Tref at 410 nm wavelength of the float glass before carrying out silver treatment and the transmittance T at 410 nm wavelength of the float glass after conducting the silver treatment. The silver treatment comprises coating the surface on the side without contact with a molten tin in a float bath with a silver paste containing silver particles, an organic solvent and a resin, baking the coated paste at 580 deg.C for 1 h in the atmosphere, forming a film having >=10μm thickness and >=95 wt.% silver content and removing the film with nitric acid.
|