LAMINATED SHEET, PRODUCTION THEREOF, AND UTILIZATION THEREOF

摘要

PROBLEM TO BE SOLVED: To provide a laminated sheet excellent in stretchability though an uppermost protective layer is sufficiently cured so as not to stick to a mold, and to obtain a composite molded object excellent in abrasion resistance, scratch resistance, chemical resistance, weatherability or the like by laminating the laminated sheet and a molded object main body. SOLUTION: A laminated sheet is obtained by laminating a clear cured layer comprising a crosslinkable compsn. with a crosslinking density of 1×10-6-5×10-3 [mol/cm3] on a sheet-like base material comprising a thermoplastic resin. In this case, a ratio of the thickness of the sheet-like base material and that of the clear cured layer is 1:0.002-1:1 and the sheet-like base material has an elongation at break of 30-300% at temp. higher than thermal deformation temp. due to an ASTM D648 method by 40 deg.C.