Elevated-temperature, plasma-transferred arc welding of nickel-base superalloy articles

摘要

A nickel-base superalloy article which is susceptible to strain-age cracking and has a directionally oriented, single crystal, or equiaxed grain structure is repaired with minimal welding heat input into the article. The article is first heated to a welding temperature of from about 1650 DEG F. to about 2000 DEG F. in an inert atmosphere. A damaged area of the article is weld repaired using a plasma-transferred arc welder which vaporizes a filler metal in a plasma arc and deposited the vaporized metal onto the article to form a weld overlay. Minimal additional heat is added to the article during welding, as the weldment metal is vaporized remotely from the article.