摘要 |
An erosion-resistant, chemically vapor-deposited zinc sulfide window and method of making the same are disclosed. The method includes the step of immersing a chemically vapor-deposited or a hot isostatic pressed, chemically vapor-deposited zinc sulfide body into a liquid comprising gallium, the liquid having a temperature of about 600 DEG C. to about 1000 DEG C., for at least about thirty minutes to form a gallium-doped body. The gallium-doped, chemically vapor-deposited zinc sulfide body according to the invention is one capable of transmitting light having a wavelength in the range of about 300 nanometers to about 15,000 nanometers. Furthermore, the gallium-doped, chemically vapor-deposited zinc sulfide window according to the invention is capable of transmitting light, having a wavelength in the range of about 380 nanometers to about 700 nanometers have been exposed to rain erosion for 20 minutes at 470 miles per hour with a 90 DEG incidence angle, with at least about 150% more efficiency than a non-doped, chemically vapor-deposited zinc sulfide window.
|