The invention relates to a composite material comprised of a coated hard metal or cermet base and to a method for the production thereof. The single layer or multilayer coating on the base contains at least one layer with a thickness ranging from 0.5 mu m to 25 mu m, at least one Al2O3 phase, and at least one phase comprised of ZrO2and/or HfO2. According to the invention, a third finely dispersive phase comprised of an oxide, oxicarbide, oxinitride or oxicarbonitride of titanium should be included in this Al2O3/ZrO2 layer and/or HfO2 layer. To this end, a CVD process is used at depositing temperatures ranging from 900 DEG C to 1000 DEG C in the gas phase under pressures ranging from 10 to 100000 Pa, whereby the gas phase, in addition to the gases essential for deposition, contains 0.2 to 5 mol % TiCl4. |