| 摘要 |
PROBLEM TO BE SOLVED: To obtain an aromatic polycarbonate resin composition reinforced with carbon fiber, having a high rigidity, a favorable mechanical strength, a favorable dimensional stability, especially an excellent impact resistance, an excellent moldability and processability and an excellent flame retardance. SOLUTION: This composition comprises 25-89 wt.% aromatic polycarbonate resin (component A), 10-55 wt.% carbon fiber (component B), 1-15 wt.% thermoplastic polyester-based resin (component C), 0-30 wt.% thermoplastic vinyl-based resin (component D) and 0-30 wt.% halogen-based flame-retardant and/or phosphoric acid ester-based flame-retardant (component E) and has 1/89-20/100 weight ratio C/A of the component C to the component A, >=70,000 kgf/cm2 elastic modulus in bending measured by ASTM D790, >=25 kgf.cm/cm reverse notched impact value and <=8 mm amount of curvature measured by ASTM D256. |