| 摘要 |
A process for manufacturing a phosphorescent screen for use in a cathode ray or field emission display, is described. The phosphor layer is applied in the form of a slurry consisting of a powdered phosphor, an ethylene glycol monobutyl ether acetate solvent, and a cellulose acetate butyrate binder. The phosphor concentration is between 30 and 60% by weight, the solvent between 5 and 52.5% and the binder between 17.5 and 35%. If the slurry composition falls within these ranges, then, once the aluminum anode layer is in place, all organic material can be removed by firing at a temperature that is less than 500 DEG C. By keeping the firing temperature below 500 DEG C., roughening of the undersurface of the aluminum is avoided and a more efficient screen is obtained. Data to illustrate this is also provided.
|