PROBLEM TO BE SOLVED: To obtain a vinyl chloride resin compsn. which is excellent in dynamic heat stability, hardly causes the adhesion of a resin to a molding machine, is excellent in moldability in long-term continuous molding, and is excellent in clarity, printability, and prevention of surface tackiness. SOLUTION: Based on 100 pts.wt. vinyl chloride resin, this compsn. contains (A) 0.5-10 pts.wt. copolymer which is prepd. from a monomer mixture comprising 5-50 mol.% long-chain (meth)acrylate having a 16-22C alkyl or alkenyl group, 40-95 mol.% glycidyl (meth)acrylate, and 0-25 mol.% other copolymerizable monomer and has a wt. average mol.wt. of 2,000-500,000 and (B) 0.01-4 pts.wt. organotin stabilizer and/or (C) 0.01-3 pts.wt. at least one metal carboxylate selected from among calcium, barium, magnesium, and zinc carboxylates. |