| 摘要 |
<p>Provided is a porcelain which is suitable as a dental porcelain capable of being fired on a ceramics core and has a low firing temperature and a low thermal expansion coefficient and which is excellent in a chemical durability. The above dental porcelain comprises glass containing silicon oxide, aluminum oxide, boron oxide, zinc oxide, sodium oxide and lithium oxide as principal components. The contents of these respective components in the above glass are 57 to 65 % by weight of SiO2, 8 to 18 % by weight of Al2O3, 15 to 25 % by weight of B2O3, 0.1 to 2 % by weight of ZnO, 3 to 7 % by weight of Na2O and 2 to 8 % by weight of Li2O respectively in terms of a percent by weight based on the total of the respective components when the respective components are reduced to SiO2, Al2O3, B2O3, ZnO, Na2O and Li2O respectively. The particularly preferred dental porcelain comprises glass having a thermal expansion coefficient of 6.0 x 10<-6> (1/ DEG C) or less as a principal structural component.</p> |