Anti-glare hard coat film and process for producing the film

摘要

An anti-glare hard coat film having a hard coat layer which has a thickness of 0.5 to 20 mu m and comprises a cured product of an ultraviolet-curing resin and agglomerates of colloidal silica particles formed with an amine compound can be obtained by coating a plastic film with a hard coat material which comprises 100 parts by weight of the ultraviolet-curing resin, 1 to 30 parts by weight as silica particles of a dispersion of colloidal silica particles, and 0.05 to 5 parts by weight of the amine compound, drying the hard coat material, and curing the dried hard coat material by irradiation of ultraviolet light. The anti-glare hard coat film has excellent surface hardness and anti-glare property and provides excellent visibility when the film is used for various types of displays.