| 摘要 |
Disclosed is a heat-resisting steel comprising 0.05 to 0.15% by weight of carbon, 0.01 to 0.1% by weight of silicon, 0.01 to 1% by weight of manganese, 8 to 11% by weight of chromium, 0.1 to 0.8% by weight of nickel, 0.1 to 0.3% by weight of vanadium, a total of 0.01 to 0.2% by weight of niobium and tantalum, 0.001 to 0.01% by weight of nitrogen, 0.01 to 0.5% by weight of molybdenum, 0.9 to 3.5% by weight of tungsten, 0.1 to 4.5% by weight of cobalt, 0.001 to 0.01% by weight of boron, and the balance being iron and incidental impurities, as well as other similar heat-resisting steels. Thus, this invention provides heat-resisting steels which are 12Cr steel-based materials having excellent high-temperature strength and can be used at steam temperatures of 593 DEG C. or above, and forged steel products such as steam turbine rotors for high-temperature use.
|