摘要 |
<p>The invention concerns an alloy based on cobalt provided with mechanical resistance to high temperature, in particular in an oxidising or corrosive environment, comprising essentially the following elements (the proportions mentioned being expressed in weight percentage of the alloy): 26 to 34 % of Cr; 6 to 12 % of Ni; 4 to 8 % of W; 2 to 4 % of Ta; 0.2 to 0.5 % of C; less than 3 % of Fe; less than 1 % of Si; less than 0.5 % of Mn; less than 0.1 % of Zr; the remainder consisting of cobalt and unavoidable impurities, the mol ratio of tantalum relative to carbon being of the order of 0.4 to 1. The invention is applicable to articles mechanically stressed at high temperature, in particular articles used for the preparation and hot transformation of glass.</p> |