| 摘要 |
There is claimed a forged structural member suitable for aerospace applications and having improved combinations of strength and toughness. The member is made from a substantially vanadium-free, lithium-free aluminum-based alloy consisting essentially of: about 4.85-5.3 wt. % copper, about 0.5-1.0 wt. % magnesium, about 0.4-0.8 wt. % manganese, about 0.2-0.8 wt. % silver, about 0.05-0.25 wt. % zirconium, up to about 0.1 wt. % silicon, and up to about 0.1 wt. % iron, the balance aluminum, incidental elements and impurities, the Cu:Mg ratio of said alloy being between about 5 and 9, and more preferably between about 6.0 and 7.5. The invention exhibits a typical longitudinal tensile yield strength of about 71 ksi or higher at room temperature and can be forged into aircraft wheels or various brake and other product forms.
|