There is provided a nickel-base alloy with service enhanced strengthening properties. When exposed to ethylene pyrolysis conditions, namely a carbon containing environment and at temperatures of at least about 900 DEG C., the alloy forms M6C and MC carbides that strengthen the alloy. The alloy may be formed into internally finned tubing. The alloy includes about 0.08-0.11% carbon, 41-45% nickel, 23-26% chromium, 0.6-0.95% manganese, 1-1.7% silicon, 0.2-0.6% titanium, 0.25-0.55% aluminum, 1.3-1.7% molybdenum, 0.25-0.6% niobium, 0.15-0.45% tantalum, 0-0.2% tungsten, 0.001-0.005% boron, 0.01-0.03% zirconium, and the balance iron with trace commercial impurities.
|