| 摘要 |
PROBLEM TO BE SOLVED: To manufacture a heat fusion transfer material to be recorded provided with an ink acceptive layer of superior acceptability for resin ink or wax molten ink, fastness of a recorded image, resistance to alteration and ink rapid drying properties for imprinted stamp and also with a magnetic recording layer to be formed as necessary. SOLUTION: An ink acceptive layer formed on one face of a sheet-shaped substrate is composed of one component selected out of gel process synthetic amorphous silica having the average particles diameter of 0.5-4 μm, apparent specific gravity of 0.1-0.3 g/cm<3> and pore volume of 0.5-2 ml/g, an aqueous bonding agent, a rosin compound and petroleum resin and containing a fastness providing agent of softening point of 65-160 deg.C and the acid value of 200 or less, and if necessary, an intermediate layer of BET specific surface area of 10-400 m<2> /g and containing a pigment of average particle diameter of 4 μm or less is formed between the sheet-shaped substrate and the acceptive layer. |