A preparation process in which PTFE coarse particles are finely pulverized into particles in wet state, thus enabling the finely pulverized particles to be washed as they are and an amount of impurities to be decreased efficiently and after the washing, agglomeration granulation is carried out, thus enabling PTFE molding powder to be obtained in the reduced number of steps; a preparation process of a polytetrafluoroethylene molding powder, characterized in that polytetrafluoroethylene coarse particles obtained by suspension polymerization of tetrafluoroethylene are finely pulverized, in wet state, into an average particle size particlularly in a range of 10 to 100 mu m and then washed; and a preparation process of a polytetrafluoroethylene molding powder, characterized in that after the washing, mechanical force is applied to the washed powder in wet state for agglomeration granulation, thus giving particles having an average particle size in a range of 200 to 800 mu m. <IMAGE> |