The Mn-Zn system ferrite according to the present invention contains main components comprising manganese oxide, zinc oxide and iron oxide, and subordinate components comprising bismuth oxide and molybdenum oxide. It comprises 22.0 to 25.0 mol% c of manganese oxide calculated as MnO, 22.0 to 25.0 mol% of zinc oxide calculated as ZnO and the remainder calculated as Fe2O3 in main components. It has been sintered after adding thereto 50 to 400 ppm of a bismuth oxide component calculated as Bi2O3 and 50 to 400 ppm of a molybdenum oxide component calculated as MoO3 as subordinate component source materials. An initial magnetic permeability at 10 KHz is 8,500 or more at -20 to 20 DEG C and 10,000 or more at 20 to 100 DEG C, and the temperature characteristics of magnetic permeability is excellent. <IMAGE> |