摘要 |
一般式: (Sr<SUB>0.9995~0.998</SUB>Eu<SUB>0.0005~0.002</SUB>)Al<SUB>2</SUB>O<SUB>4</SUB>·(Sr<SUB>0.9995~0.998</SUB>Eu<SUB>0.0005~0.002</SUB>)O·n(Al<SUB>1-a-b</SUB>B<SUB>b</SUB>Dy<SUB>a</SUB>)<SUB>2</SUB>O<SUB>3</SUB>式中a=0.0005~0.002b=0.001~0.35n=1~8所表示的长余辉高亮度发光材料及其制造方法,本发光材料以SrCO<SUB>3</SUB>,α型Al<SUB>2</SUB>O<SUB>3</SUB>,γ型Al<SUB>2</SUB>O<SUB>3</SUB>,硼化合物,Eu<SUB>2</SUB>O<SUB>3</SUB>,Dy<SUB>2</SUB>O<SUB>3</SUB>为原料,以碳粉造成还原气氛,将充分混合的原料在7~10小时内从400℃缓慢升温至1250℃~1600℃,保温5~3小时后再缓慢降温至200℃,然后经粉碎和分粒而制成。 |